Non-asbestos friction-material composition, and friction material and friction member using same

ABSTRACT

A non-asbestos frictional material composition is provided, which is capable of provide a frictional material with excellent shear strength, anti-crack properties, and abrasion resistance, even with the reduced content of copper. Furthermore, a frictional material and a friction member formed by using this non-asbestos frictional material composition are provided. The non-asbestos frictional material composition containing a binder, an organic filler, an inorganic filler, and a fiber base material includes: copper in a content of 0.5 mass % or less as a copper element; a metal other than copper and copper alloy in a content of 0.5 mass % or less; an acrylic elastomer-dispersed phenol resin as the binder in a content of 7-15 mass %; and Ca(OH) 2  and/or CaO as the inorganic filler in a content of 1-5 mass %.

TECHNICAL FIELD

The present invention relates to a non-asbestos frictional material composition, and a frictional material and a friction member formed by using the composition. Specifically, the present invention relates to a non-asbestos frictional material composition with low environmental load due to the low content of copper and with excellent shear strength, anti-crack properties, and abrasion resistance, which is appropriate for frictional materials such as a disc brake pad and a brake lining to brake a car and the like. The present invention further relates to a frictional material and a friction member formed by using this non-asbestos frictional material composition.

BACKGROUND ART

Frictional materials such as a disc brake pad and a brake lining are used for braking a car and the like. The frictional materials play a role in the brake by frictioning facing members such as a disc rotor and a brake drum. Therefore, for the frictional materials, not only increasing and stabilizing the friction coefficient but also hardly wearing the disc rotor that is a facing member (anti-rotor-abrasion resistance), hardly generating the squeal (squeal properties), and prolonging the life of the pad (abrasion resistance) are required. The durability performance such as no shearing during the braking at a high load (shear strength) or no cracks by the high temperature braking history (anti-crack properties) are also required.

A frictional material includes a binder, a fiber base material, an inorganic filler, and an organic filler, generally in combination with one or two or more kinds thereof to provide the above-mentioned properties. As the fiber base material, an organic fiber, a metal fiber, an inorganic fiber, and the like are used. To improve the anti-crack properties and the abrasion resistance, a copper fiber and a copper alloy fiber are generally used as the metal fiber. To further improve the abrasion resistance, chips and powders of copper and copper alloy may be used. As the frictional material, a non-asbestos frictional material is a mainly used, which is formed by using a large amount of copper, copper alloy, and the like.

However, the frictional material containing copper and copper alloy generates abrasion powder containing copper during the braking. Since it is suggested that the abrasion powder leads to pollution of rivers, lakes, and oceans, there is a movement accelerated to control the use of the non-asbestos frictional material. To provide a frictional material containing no copper or copper alloy with excellent friction coefficient, abrasion resistance, and rotor abrasion resistance, it is proposed that the frictional material for the brake with a fiber base material, a binder, and a friction adjustment component do not contain a heavy metal or a heavy-metal compound and that the frictional material contains magnesium oxide and graphite in a content of 45-80 vol %, in which the ratio of magnesium oxide to graphite is 1/1-4/1 (see to Patent document 1).

CITATION LIST

Patent document 1: JP 2002-138273A

DISCLOSURE OF THE INVENTION

However, the frictional material for the brake of Patent document 1 hardly satisfies all of the shear strength, the anti-crack properties, and the abrasion resistance.

On the other hand, as metal fibers other than a copper fiber contained in the frictional material, iron fibers such as a steel fiber and a cast iron fiber are used for the purpose of improving the anti-crack properties. However, iron fibers have a disadvantage of the high aggression to a facing member. Nonferrous metal fibers such as a zinc fiber and an aluminum fiber generally used for a frictional material as metal fibers other than a copper fiber often have a low heatproof temperature compared with a copper fiber and an iron fiber. This causes a problem of the deteriorated abrasion resistance of the frictional material.

An inorganic fiber is used to improve the anti-crack properties of the frictional material. However, to obtain the satisfied anti-crack properties, a large amount of inorganic fiber should be added. This causes a problem of the deteriorated abrasion resistance.

It is known that the use of graphite can improve the abrasion resistance of the frictional material. However, to obtain the satisfied anti-crack properties, a large amount of graphite should be added. This causes a problem of the substantially lowered friction coefficient.

As mentioned above, the frictional material containing the reduced content of copper has poor shear strength, abrasion resistance, and anti-crack properties and hardly satisfies all of the shear strength, the anti-crack properties, and the abrasion resistance.

In view of such a background, the objective of the present invention is to provide a non-asbestos frictional material composition capable of providing a frictional material with excellent shear strength, anti-crack properties, and abrasion resistance, and also providing a frictional material and a friction member formed by using this non-asbestos frictional material composition, even with the reduced content of copper possibly causing pollution of rivers, lakes, oceans and the like.

As a result of their great effort, the present inventors have found that the above-mentioned problem can be solved by a non-asbestos frictional material composition containing a copper and a metal other than copper and copper alloy at a certain level or less and essentially containing a specific amount of an acrylic elastomer-dispersed phenol resin as a binder, and a specific amount of Ca (OH) ₂ and/or CaO as a mineral filler so as to achieve the present invention.

The present invention is as follows.

(1) A non-asbestos frictional material composition containing a binder, an organic filler, an inorganic filler, and a fiber base material includes: copper in a content of 0.5 mass % or less as a copper element; a metal other than copper and copper alloy in a content of 0.5 mass % or less; an acrylic elastomer-dispersed phenol resin as the binder in a content of 7-15 mass %; and Ca(OH)₂ and/or CaO as the inorganic filler in a content of 1-5 mass %.

(2) A frictional material being formed from the non-asbestos frictional material composition according to (1).

(3) A friction member being formed from the frictional material formed from the non-asbestos frictional material composition according to (1) and a backing plate.

Advantageous Effects of the Invention

When used for frictional materials such as a disc brake pad and a brake lining for a car, the non-asbestos frictional material composition of the present invention has low environmental load due to the low content of copper in abrasion powder generated during the braking and can provide excellent shear strength, anti-crack properties, and abrasion resistance. The use of the non-asbestos frictional material composition of the present invention can provide a frictional material and a friction member with the above-mentioned properties.

PREFERRED MODE FOR CARRYING OUT THE INVENTION

The non-asbestos frictional material composition of the present invention, and a frictional material and a friction member formed by using the composition will be described in detail below. In the present invention, the non-asbestos frictional material composition, the non-asbestos frictional material, and the non-asbestos friction member are referred to as a frictional material composition, a frictional material, and a friction member which do not substantially contain asbestos, respectively. The non-asbestos frictional material composition is sometimes simply referred to as “frictional material composition,” the non-asbestos frictional material as “frictional material,” and the non-asbestos friction member as “friction member.”

Non-Asbestos Frictional Material Composition

The non-asbestos frictional material composition of the present invention containing a binder, an organic filler, an inorganic filler, and a fiber base material includes: copper in a content of 0.5 mass % or less as a copper element; a metal other than copper and copper alloy in a content of 0.5 mass % or less; an acrylic elastomer-dispersed phenol resin as the binder in a content of 7-15 mass %; and Ca (OH) ₂ and/or CaO as the inorganic filler in a content of 1-5 mass %.

According to this structure, a frictional material and a friction member formed by using the non-asbestos frictional material composition of the present invention has low environmental load due to the low content of copper in abrasion powder generated during the braking and provides excellent shear strength, anti-crack properties, and abrasion resistance, compared with conventional ones.

In the present invention, “the content of copper as a copper element” is referred to as the total content of copper as a copper element in a material containing copper alone, copper alloy, copper oxide, copper sulfide, a copper complex, and the like. The content of the copper as a copper element adjusted to 0.5 mass % or less can reduce the environmental load of the frictional material to be lower than that of conventional ones.

In the present invention, “metal other than copper and copper alloy” is referred to as a metal alone other than copper and an alloy not containing copper. For example, such a metal falls under a material mainly containing a metal such as aluminum, iron, zinc, tin, titanium, zirconium, nickel, chromium, magnesium, silicon, or germanium, alone or the alloy thereof, or cast iron. The form includes, for example, the fiber and the powder of the above-mentioned metal alone or alloy.

The non-asbestos frictional material composition of the present invention should contain a metal other than copper and copper alloy in a content of 0.5 mass % or less, preferably do not substantially contain it (0 mass %). This can prevent the abrasion resistance of the frictional material from deteriorating.

In the present invention, “the content of a metal other than copper and copper alloy” does not include that of a metal element contained in a metal oxide, a metal sulfide, a metal complex, and the like.

Each of the components contained in the frictional material composition of the present invention will be explained.

(Binder)

The binder binds an organic filler, an inorganic filler, a fiber base material, and the like in the frictional material composition to provide strength.

The non-asbestos frictional material composition of the present invention contains an acrylic elastomer-dispersed phenol resin as the binder in a content of 7-15 mass % as the essential component from the viewpoint of improving the shear strength, the anti-crack properties, the abrasion resistance, and the like.

In the non-asbestos frictional material composition of the present invention, the content of the above-mentioned acrylic elastomer-dispersed phenol resin adjusted to 7 mass % or more provides excellent shear strength, anti-crack properties, and abrasion resistance. The content adjusted to 15 mass % or less can reduce the porosity of the frictional material and prevent the deteriorated sound vibration performance such as squeal due to the high elastic modulus. The content of the above-mentioned acrylic elastomer-dispersed phenol resin is preferably 8-15 mass %, more preferably 10-15 mass %, from the viewpoint of improving the shear strength.

The acrylic elastomer-dispersed phenol resin is a phenol resin in which an acrylic elastomer is dispersed. The above-mentioned acrylic elastomer-dispersed phenol resin includes, for example, MILEX RN-2830MR, RN-2830MB, and RN-2410MB which are commercially available from Mitsui Chemicals, Inc.

In the non-asbestos frictional material composition of the present invention, the above-mentioned acrylic elastomer-dispersed phenol resin can be used as the main component of the binder in combination with a binder other than this phenol resin. As the binder other than the acrylic elastomer-dispersed phenol resin, any binders can be used without any limitation in particular as long as being thermosetting resins typically used as a binder of the frictional material.

The above-mentioned thermosetting resins include, for example, a phenol resin; various elastomer-dispersed phenol resins such as a silicone elastomer-dispersed phenol resin; and various modified phenol resins such as an acrylic-modified phenol resin, a silicone-modified phenol resin, a cashew-modified phenol resin, an epoxy-modified phenol resin, and an alkylbenzene-modified phenol resin. These can be used alone or in combination with two or more kinds thereof. In particular, when a binder other than the acrylic elastomer-dispersed phenol resin is used, a phenol resin, an acrylic-modified phenol resin, a silicone-modified phenol resin, and an alkylbenzene-modified phenol resin are preferable for providing excellent heat resistance, moldability, and friction coefficient.

The content of the above-mentioned binder, including an acrylic elastomer-dispersed phenol resin, in the non-asbestos frictional material composition of the present invention is preferably 5-20 mass %, more preferably 5-15 mass %, further more preferably 7-15 mass %. The content of the binder adjusted to 5-20 mass % can further prevent the reduced strength of the frictional material and the deterioration of the sound vibration performance such as squeal due to the reduced porosity and the increased elastic modulus of the frictional material.

(Organic Filler)

The organic filler is contained as a friction modifier to improve the sound vibration performance, the abrasion resistance, and the like of the frictional material.

As the organic filler contained in the non-asbestos frictional material composition of the present invention, any organic fillers can be used without any limitation in particular as long as delivering the above-mentioned performance. Cashew dust, a rubber component, and the like can typically be used as organic fillers.

As the above-mentioned cashew dust, any cashew dust, which is obtained by grinding cured cashew nut shell oil, may be used as long as typically used for a frictional material. The above-mentioned rubber component includes, for example, natural rubber, acrylic rubber, isoprene rubber, polybutadiene rubber (BR), nitrile-butadiene rubber (NBR), and styrene-butadiene rubber (SBR). These can be used alone or in combination with two or more kinds thereof.

The cashew dust and the rubber component may be used together, or the cashew dust coated with the rubber component may be used. As the organic filler, the cashew dust and the rubber component is preferably used together from the viewpoint of the sound vibration performance.

The content of the above-mentioned organic filler in the non-asbestos frictional material composition of the present invention is preferably 1-20 mass %, more preferably 1-15 mass %, further more preferably 5-15 mass %. The content of the organic filler adjusted to 1-20 mass % can prevent the increased elastic modulus of the frictional material, the deteriorated sound vibration performance such as squeal, the deteriorated heat resistance, and the reduced strength due to the heat history. When the cashew dust and the rubber component are used together, the mass ratio of the cashew dust to the rubber component (cashew dust/rubber component) preferably falls within the range of 0.2-10, more preferably 0.3-5.

(Inorganic Filler)

The inorganic filler is contained as a friction modifier to prevent the heat resistance of the frictional material from deteriorating.

The non-asbestos frictional material composition of the present invention contains Ca(OH)₂ and/or CaO as the inorganic filler in a content of 1-5 mass % in total as the essential component. The content of the above-mentioned Ca(OH)₂ and/or CaO adjusted to 1 mass % or more in total can provide excellent shear strength, anti-crack properties, and abrasion resistance. The content adjusted to 5 mass % or less in total can prevent the abrasion resistance from deteriorating.

For the non-asbestos frictional material composition of the present invention, an inorganic filler other than the above-mentioned Ca(OH)₂ and CaO can be used together.

As the inorganic filler other than Ca(OH)₂ and CaO, any inorganic fillers can be used without limitation in particular as long as being inorganic fillers typically used for the frictional material.

The inorganic filler other than Ca(OH)₂ and CaO includes, for example, antimony trisulfide, tin sulfide, molybdenum disulfide, iron sulfide, bismuth sulfide, zinc sulfide, sodium carbonate, calcium carbonate, magnesium carbonate, barium sulfate, dolomite, coke, graphite, mica, iron oxide, vermiculite, granular potassium titanate, calcium sulfate, plate-like potassium titanate, talc, clay, zeolite, zirconium silicate, zirconium oxide, mullite, chromite, titanium oxide, magnesium oxide, silica, iron oxide, and an activated alumina such y alumina. These can be used alone in combination with two or more kinds thereof. From the viewpoint of decreasing the aggressiveness to a facing member, graphite and barium sulfate are preferably contained.

The content of the above-mentioned inorganic filler, including Ca(OH)₂ and CaO, in the non-asbestos frictional material composition of the present invention is preferably 30-80 mass %, more preferably 50-80 mass %, furthermore preferably 50-70 mass %. The content of the inorganic filler adjusted to 30-80 mass % can prevent the heat resistance from deteriorating.

(Fiber Base Material)

The fiber base material exhibits a reinforcement effect on the improvement of the mechanical strength and the like of the frictional material.

The fiber base material used in the present invention includes an inorganic fiber, a metal fiber, an organic fiber, and a carbon fiber. These can be used alone or in combination with two or more kinds thereof.

The above-mentioned inorganic fiber includes a ceramic fiber, a biodegradable ceramic fiber, a mineral fiber, a glass fiber, a potassium titanate fiber, a silicate fiber, and wollastonite. These can be used alone or in combination with two or more kinds thereof.

Among these inorganic fibers, a potassium titanate fiber and a ceramic fiber, which are easily inhaled into a human body, are preferably not contained, but a biodegradable ceramic fiber and a biodegradable mineral fiber contained in any combination with SiO₂, Al₂O₃, CaO, MgO, FeO, Na₂O, and the like are preferable, from the viewpoint of decreasing the environmental load material.

The mineral fiber is referred herein to as an artificial inorganic fiber in which blast furnace slag for slag wool, basalt for basalt fiber, and other natural stone are melt-spun as the main component. The mineral fiber is preferably a natural mineral containing an Al element. Specifically, the mineral fiber containing SiO₂, Al₂O₃, CaO, MgO, FeO, Na₂O, and the like alone or in combination with two or more kinds thereof can be used. Preferably, the mineral fiber containing an Al element can be used. As the mean fiber length of the total mineral fiber contained in the frictional material composition increases, the bond strength with each of the components of the frictional material composition tends to be decreased. Therefore, the mean fiber length of the entire mineral fiber is preferably 500 μm or less, more preferably 100-400 μm. The mean fiber length is referred herein to as the number average fiber length indicating the average length of the total corresponding fibers. For example, the mean fiber length of 200 μm indicates that the average length of 50 mineral fibers which are randomly selected and then measured with a light microscope is 200 μm.

The mineral fiber used in the present invention is preferably biosoluble from the viewpoint of the harmful effect on a human body. The biosoluble mineral fiber is referred herein to as a mineral fiber with the feature to be partially broken down in a short time and eliminated from the body even when entering a human body. Specifically, the biosoluble mineral fiber denotes a fiber satisfying the condition in which the chemical composition shows that the total content of an alkali oxide and an alkaline earth oxide (oxides of sodium, potassium, calcium, magnesium, and barium) is 18 mass % or more, in which the short-term continuous aspiration test shows the half-life of 20 μm or more of fiber is 40 days or less, in which the intraperitoneal test shows no evidence for excessive carcinogenic properties, or in which the long-term continuous aspiration test shows no associated pathogenesis or tumorigenesis (Nota Q of EU directive 97/69/EC (exempted from the carcinogenic classification)). Such a biodegradable mineral fiber includes SiO₂—Al₂O₃—CaO—MgO—FeO—Na₂O-type fiber, and a fiber containing SiO₂, Al₂O₃, CaO, MgO, FeO, and Na₂O in any combination thereof. The commercially available product includes the Roxul fibers produced by LAPINUS FIBRES B.V. The Roxul contains SiO₂, Al₂O₃, CaO, MgO, FeO, and Na₂O.

As the above-mentioned metal fiber, a copper fiber or a copper alloy fiber can be used to improve the anti-crack properties and the abrasion resistance. The copper fiber or the copper alloy fiber includes a copper fiber, a brass fiber, and a bronze fiber. These can be used alone or in combination with two or more kinds thereof.

However, when the copper fiber or the copper alloy fiber is contained, the total content of copper in the non-asbestos frictional material composition of the present invention should fall within the range of 0.5 mass % or less as a copper element in view of the environmental load.

As the above-mentioned metal fiber, a metal fiber other than a copper fiber and a copper alloy fiber may be used from the viewpoint of improving the friction coefficient and the anti-crack properties. The metal fiber other than a copper fiber and a copper alloy fiber includes, for example, fibers of metals such as aluminum, iron, zinc, tin, titanium, nickel, magnesium, silicon alone, or the alloy thereof, and a fiber mainly containing metal, such as a cast iron fiber. These can be used alone or in combination with two or more kinds thereof.

From the viewpoint of the abrasion resistance, the content of a metal other than copper and copper alloy in the non-asbestos frictional material composition of the present invention should fall within the range of 0.5 mass % or less. From the viewpoint of improving the abrasion resistance, no metal fibers other than a copper fiber and a copper alloy fiber are preferably contained (0 mass %).

In the present invention, the organic fiber is referred to as a fibrous material mainly containing an organic substance but not as the below-mentioned carbon fibers and used to improve the anti-crack properties and the abrasion resistance, and the like.

The above-mentioned organic fiber includes an aramid fiber, a cellulose fiber, an acrylic fiber, and a phenol resin fiber (with a cross-linked structure). These can be used alone or in combination with two or more kinds thereof. As the organic fiber, an aramid fiber is preferably used from the viewpoint of the abrasion resistance.

The above-mentioned carbon fiber includes a flame-resistant fiber, a pitch-based carbon fiber, a polyacrylonitrile (PAN) carbon fiber, and an active carbon fiber. These can be used alone or in combination with two or more kinds thereof.

The content of the above-mentioned fiber base material in the non-asbestos frictional material composition of the present invention is preferably 5-40 mass %, more preferably 5-30 mass %, furthermore preferably 5-20 mass %. The content of the fiber base material adjusted to 5-40 mass % provides an appropriate porosity as the frictional material so as to prevent the deteriorated sound vibration performance such as squeal due to the high elastic modulus . Appropriate material strength and appropriate abrasion resistance are also provided so that the moldability can also be improved.

(Other Materials)

In the non-asbestos frictional material composition of the present invention, materials other than the binder, the organic filler, the inorganic filler, and the fiber base material can optionally be blended.

For example, to improve the abrasion resistance, an organic additive including a fluorine polymer such as polytetrafluoroethylene (PTFE) can be blended.

Frictional Material and Friction Member

The present invention also provides a frictional material and a friction member formed by using the above-mentioned non-asbestos frictional material composition.

The non-asbestos frictional material composition of the present invention can be molded for the use as frictional materials such as a disc brake pad and a brake lining for a car. The frictional material of the present invention exhibits excellent friction coefficient, anti-crack properties, and abrasion resistance and is therefore suitable for a disc brake pad with a large load during the braking.

Through the use of the above-mentioned frictional material, a friction member, which is formed so that the frictional material is the frictional surface, can be obtained. The friction member of the present invention that can be formed by using the frictional material includes, for example, the following structures.

Structure (1) : Only the frictional material is contained. Structure (2) : A backing plate and the frictional material consisting of the non-asbestos frictional material composition of the present invention are contained, in which the frictional material is formed to be the frictional surface on the backing plate. Structure (3) : In the structure (2), a primer layer to modify the surface for improving the adhesive effect of the backing plate and an adhesive layer to bond the backing plate with the frictional material are placed between the backing plate and the frictional material.

The above-mentioned backing plate is typically used for a friction member to improve the mechanical strength of the friction member. As the material of the backing plate, a metal, a fiber-reinforced plastic, or the like can be used. The material, for example, includes iron, stainless steel, inorganic fiber-reinforced plastic, and a carbon fiber-reinforced plastic. As the primer layer and the adhesive layer, any materials may be used as long as used for a friction member such as a brake shoe.

The frictional material of the present invention can be fabricated using a generally used method by molding, preferably hot press-molding the non-asbestos frictional material composition of the present invention.

Specifically, the non-asbestos frictional material composition of the present invention is uniformly mixed by using a mixer such as a Loedige mixer, a pressure kneader, and an Eirich intensive mixer. The mixture is preformed in a mold. The obtained preformed material is molded under the condition at a molding temperature of 130-160° C. and a molding pressure of 20-50 MPa for 2-10 minutes. The obtained molded product is heated at 150-250° C. for 2-10 hours. The frictional material can be fabricated by coating, scorching, and polishing as needed.

The frictional material formed from the non-asbestos frictional material composition is useful as the “over layer” of friction members such as a disc brake pad and a brake lining due to excellent friction coefficient, anti-crack properties, and abrasion resistance. The frictional material can be used for being formed as the “under layer” of friction members due to the high anti-crack properties as the frictional material.

The “over layer” is the frictional material formed so as to be the frictional surface of the friction member. The “under layer” is a layer placed between the frictional material formed to be the frictional surface of the friction member and the backing plate in order to improve the shear strength and the anti-crack properties around the part bonding the frictional material with the backing plate.

EXAMPLES

The non-asbestos frictional material composition, the frictional material, and the friction member of the present invention will be described in detail in reference to Examples and Comparative examples. However, the present invention is not limited to these examples.

Examples 1-5 and Comparative Examples 1-5 (Production of Disc Brake Pad)

The materials were blended according to the blend ratio shown in Table 1 to obtain the frictional material compositions of Examples 1-5 and Comparative examples 1-5. Each of the frictional material compositions was mixed using a Loedige mixer (available from MATSUBO Corporation, brand name: Loedige mixer M20). This mixture was preformed with a molding press (available from OJIKIKAI CO., LTD). The obtained preformed material was hot press-molded together with an iron backing plate (available from Hitachi Automotive Systems, Ltd.) using a molding press (SANKI SEIKO CO., LTD.) under the condition at a molding temperature of 145° C. and a molding pressure of 30 MPa for 5 minutes. The obtained molded article was heated at 200° C. for 4.5 hours, polished with a rotary polisher, and then scorched at 500° C. to obtain the disc brake pads of Examples 1-5 and Comparative examples 1-5. In these examples and comparative examples, disc brake pads with having a backing plate thickness of 6 mm, a frictional material thickness of 11 mm, and a frictional material projected area of 52 cm² were produced.

(Evaluation of Shear Strength)

The shear strength was measured based on Japan Industrial Standard JIS D4422.

(Evaluation of Anti-Crack Properties)

The braking was repeated at a brake temperature of 400° C. (initial speed: 50 km/h, closing speed: 0 km/h, deceleration: 0.3 G, brake temperature before braking: 100° C.) based on JASO C427 until the thickness of the each frictional material was reduced to half. The generation of cracks on the side face and the frictional surface of the each frictional material was measured. The generation of cracks was evaluated with the following scores 1-3.

Score 1: No cracks were generated. Score 2: Cracks were generated to the extent where a 0.1 mm thickness gauge does not enter the frictional surface or the side face of the frictional material. Score 3: Cracks were generated to the extent where a 0.1 mm thickness gauge enters the frictional surface or the side face of the frictional material.

When cracks were generated to the extent where a 0.1 mm thickness gauge does not enter one of the frictional surface and the side face of the frictional material but enters the other, the generation of cracks was evaluated as Score 3.

(Evaluation of Abrasion Resistance)

The abrasion resistance was measured based on Japanese Automotive Standards Organization JASO C427. The abrasion loss of the each frictional material, which corresponds to 1000 times of braking at brake temperatures of 100° C. and 300° C., were evaluated.

The friction coefficient, the abrasion resistance, and the anti-crack properties were evaluated at an inertia of 7 kgf·m·s² with a dynamometer (available from SANKI SEIKO CO., LTD.) based on the above-mentioned JASO C406 and JASO C427. The above-mentioned evaluation was carried out using a ventilated disc rotor (material: FC190, available from KIRIU Corporation) and a general pin sliding collet type caliper.

The evaluation results are shown in Table 1.

Details of the each structural component shown in Table 1 are as follows.

(Binder)

Acrylic elastomer-dispersed phenol resin: available from Mitsui Chemicals, Inc (brand name: MILEX RN-2830MB, amount of acrylic elastomer: 30 parts by mass)

(Organic Filler)

Cashew dust: available from Tohoku Chemical Industries, Ltd (brand name: FF-1056, maximum particle size: 500 μm)

(Inorganic Filler)

Barium sulfate: available from SAKAI CHEMICAL INDUSTRY CO., LTD. (brand name: Barium sulfate BA)

Calcium carbonate: available from TAKEHARA KAGAKU KOGYO CO., LTD. (brand name: SUN LIGHT)

Mica: available from Imerys (brand name: 325HK)

Graphite: available from TIMCAL (brand name: KS75)

Potassium titanate: available from Kubota Corporation (Brand name: TXAX-MA, plate-like potassium titanate)

Ca (OH) ₂: available from Chichibu Lime Industry CO. , LTD (brand name: SA-149)

CaO: available from Ohmi Chemical Industry CO., LTD. (brand name: CML-31)

(Organic Fiber)

Aramid fiber: available from DU PONT-TORAY CO., LTD. (brand name: 1F538)

(Metal Fiber)

Copper fiber: available from Sunny Metal (brand name: SCA-1070)

Iron fiber: available from GMT (brand name: #0)

(Inorganic Fiber)

Mineral fiber: available from LAPINUS FIBRES B.V (brand name: RB240Roxul 1000, mean fiber length: 300 μm)

TABLE 1 Examples Comparative examples 1 2 3 4 5 1 2 3 4 5 Frictional Binder Acrylic 7 15 12 7 15 10 6 16 9 7 material elastomer- composition dispersed (mass %) phenol resin Organic filler Cashew dust 4 4 4 4 4 4 4 4 4 4 SBR powder 4 4 4 4 4 4 4 4 4 4 Inorganic filler Barium sulfate 27 15 21 23 18 15 29 13 25 20 Calcium 13 13 13 13 13 13 13 13 13 13 hydroxide Mica 7 7 7 7 7 7 7 7 7 7 Graphite 7 7 7 7 7 7 7 7 7 7 Potassium titanate 10 10 10 10 10 10 10 10 10 10 Ca(OH)₂ 1 5 2 3 1 — — — — 8 CaO — — — 2 1 — — 6 — — Fiber base material Aramid fiber 4 4 4 4 4 4 4 4 4 4 Copper fiber — — — — — 10 — — — — Iron fiber — — — — — — — — 1 — Mineral fiber 16 16 16 16 16 16 16 16 16 16 Content of copper as copper element (mass %) 0 0 0 0 0 10 0 0 0 0 Content of metal other than copper 0 0 0 0 0 0 0 0 1 0 and copper alloy (mass %) Evaluation Shear strength (MPa) 6.6 7.3 7.3 6.8 7.0 7.2 4.3 6.1 6.0 4.0 Anti-crack properties Score 1 Score 1 Score 1 Score 1 Score 1 Score 1 Score 3 Score 2 Score 2 Score 3 Abrasion resistance 100° C. 0.11 0.11 0.10 0.11 0.12 0.10 0.14 0.12 0.13 0.13 (mm/1000 brakings) 300° C. 1.05 1.08 1.01 1.04 1.07 1.01 1.68 1.44 1.31 1.40

Examples 1-5 exhibit shear strength, anti-crack properties, and abrasion resistance on about the same level as those of Comparative example 1 containing a large amount of copper. Furthermore, Examples 1-5 have excellent shear strength, anti-crack properties, and abrasion resistance compared with Comparative example 2 containing no copper, Ca(OH)₂ or CaO but a metal other than copper and copper alloy in a content of 0.5 mass % or less and an acrylic elastomer-dispersed phenol resin in a content of less than 7 mass %; Comparative example 3 containing no copper but a metal other than copper and copper alloy in a content of 0.5 mass % or less, an acrylic elastomer-dispersed phenol resin in a content of more than 15 mass %, and CaO in a content of more than 5 mass %; Comparative example 5 containing Ca(OH)₂ in a content of more than 5 mass %; and Comparative example 4 containing no Ca(OH)₂ or CaO but a metal other than copper and copper alloy in a content of more than 0.5 mass %.

INDUSTRIAL APPLICABILITY

The non-asbestos frictional material composition of the present invention, and a frictional material and a friction member formed by using the composition have low environmental load due to the low content of copper in abrasion powder generated during the braking, can provide excellent shear strength, anti-crack properties, and abrasion resistance and are therefore suitable for a brake pad for a car and the like, compared with conventional ones. 

1. A non-asbestos frictional material composition containing a binder, an organic filler, an inorganic filler, and a fiber base material, comprising: copper in a content of 0.5 mass % or less as a copper element; a metal other than copper and copper alloy in a content of 0.5 mass % or less; an acrylic elastomer-dispersed phenol resin as the binder in a content of 7-15 mass %; and Ca(OH)₂ and/or CaO as the inorganic filler in a content of 1-5 mass %.
 2. A frictional material being formed from the non-asbestos frictional material composition according to claim
 1. 3. A friction member being formed from a frictional material formed from the non-asbestos frictional material composition according to claim 1 and a backing plate. 